牌号简介 About |
---|
填充。非溴化、非氯化FR系统。UL94 V0 / 5va额定。相对温度指数( 电气特性=95/冲击负荷=80/静态下=95)。介电强度。适用于电子/电子,市场应用。典型性能 |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲强度 bending strength |
|||
屈服,2 mm/min Yield, 2 mm/min |
87 | MPa | ISO 178 |
屈服,2.60 mm/min,50 mm跨度 Yield, 2.60 mm/min, 50 mm span |
91 | MPa | ASTM D790 |
屈服,1.30 mm/min,50 mm跨度 Yield, 1.30 mm/min, 50 mm span |
98 | MPa | ASTM D790 |
弯曲模量 Bending modulus |
|||
2 mm/mim 2 mm/mim |
2350 | MPa | ISO 178 |
2.60 mm/min,100 mm跨距 2.60 mm/min, 100 mm span |
2300 | MPa | ASTM D790 |
1.30 mm/min,50 mm跨距 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
泰伯磨损 Taber wear and tear |
|||
CS-17,1 kg CS-17,1 kg |
mg/1000cy | ASTM D1044 | |
拉伸强度 tensile strength |
|||
断裂,I型,50 mm/min Fracture, Type I, 50 mm/min |
MPa | ASTM D638 | |
断裂,50 mm/min Fracture, 50 mm/min |
MPa | ISO 527 | |
屈服,I型,50 mm/min Yield, Type I, 50 mm/min |
MPa | ASTM D638 | |
屈服,50 mm/min Yield, 50 mm/min |
MPa | ISO 527 | |
拉伸应变 Tensile strain |
|||
断裂,Ⅰ型,50 mm/min Fracture, Type I, 50 mm/min |
% | ASTM D638 | |
断裂,50 mm/min Fracture, 50 mm/min |
% | ISO 527 | |
屈服,Ⅰ型,50 mm/min Yield, Type I, 50 mm/min |
% | ASTM D638 | |
屈服,50 mm/min Yield, 50 mm/min |
% | ISO 527 | |
拉伸模量 Tensile modulus |
|||
50 mm/min 50 mm/min |
MPa | ASTM D638 | |
1 mm/min 1 mm/min |
MPa | ISO 527 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D 4812 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,80*10*4 23℃,80*10*4 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ |
J/m | ASTM D256 | |
仪表冲击总能量 Total energy of instrument impact |
|||
23℃ 23℃ |
J | ASTM D 3763 | |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/2C | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span |
℃ | ISO 75/Af | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span |
℃ | ISO 75/Bf | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
热导率 Thermal conductivity |
W/m-℃ | ASTM C 177 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
B50 B50 |
℃ | ASTM D1525 | |
相对温度指数 Relative temperature index |
|||
非机械冲击性能 Non mechanical impact performance |
℃ | UL 746B | |
电气性能 Electrical performance |
℃ | UL 746B | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746B | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
溶体流动速率 280℃/5.0 kgf Solution flow rate 280 ℃/5.0 kgf |
g/10 min | ASTM D 1238 | |
熔体体积流动速率 Melt Volume Rate |
|||
280℃,5 kg 280℃,5 kg |
cm³/10min | ISO 1133 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
绝缘强度 Insulation strength |
|||
在油中 In oil |
kV/mm | ASTM D 149 | |
相对电容率 Relative permittivity |
|||
100 kHz 100 kHz |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
消散因素 Dissipation factors |
|||
100kHz 100kHz |
- | ASTM D 150 | |
100Hz 100Hz |
- | ASTM D 150 | |
耐电弧性 Arc resistance |
|||
钨丝 Tungsten wire |
PLC Code | ASTM D495 | |
电阻丝点火 Resistance wire ignition |
PLC Code | UL 746A | |
高压火弧电阻 High voltage arc resistance |
PLC Code | UL 746A | |
高电流电弧点火 High current arc ignition |
|||
表面 surface |
PLC Code | UL 746A | |
相比漏电起痕指数 Compared to the leakage tracing index |
PLC Code | UL 746A | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.01 mm 1.01 mm |
UL 94 | ||
1.47 mm 1.47 mm |
UL 94 | ||
2.99 mm 2.99 mm |
UL 94 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
大同机械盈利预警 盈余额将明显增加
2017-02-21 据大同机械2月17日发布全年盈利公告显示,截至2016年12月31日止,大同机械集团预计该财政年度公司股权持有人应占亏损,将会较2015年财政年度出现的约3881.7万港元亏损显著增加。 |
大同机械盈利预警 盈余额将明显增加 据大同机械2月17日公布全年度赢利公示显示信息,截止2016年12月31日止,大同机械集团公司预估该财年公司股权持有者应占亏损,可能较2015年财年出現的约3881.8万港币亏损明显提升。 国内制造业低迷致亏损增加 回望大同机械2016年半年度财务报告显示信息,一样因为中国大陆加工制造业低迷这一缘故,2016年上半年度大同机械收益为10.83亿港元,同比减少12.7%;利润率为1.79亿港元,利润率为16.5%,与2015年同比增加小涨0.2%。 上半年度亏损为4088万港币,全年度亏损将超出2015年的3881.8万港币亏损额。比照由此可见,国内制造业竞争仍在加重,将来大同机械各类指标值改进仍有很大难度系数。 亏损剖析 公示强调,大同机械亏损关键缘故:第一,中国大陆经济发展变缓,尤其是加工制造业,进而造成 大同机械营业收入降低;第二,为了更好地从关键竞争者中得到大量的市场占有率而调节营销策略,造成 毛利率降低;第三,资产重组计划令支出提升,尤其是注塑制品及生产加工业务流程各分部及其机械设备制造业务流程各分部上年的运营亏损较2015年明显提升。 资产重组计划关键在注塑机业务流程 在其中,大同机械资产重组计划为,关掉俩家机械设备制造企业:东莞市明新虫胶产品和东莞市大同市数控设备,并关键提升东莞工厂技术专业注塑机生产能力和提高无锡市加工厂中大中型注塑机生产能力。 该资产重组计划说明,大同机械将来将把重心点下注在注塑机上。近些年大同机械注塑机有不错的发展趋势,但最近中下游要求逐渐皮软。据大同机械2016上半年度财务报告显示信息,其注塑制品及生产加工业务流程销售额为1.9亿港元,同比减少17%。因而,大同机械关键发展趋势注塑机而产生的销售业绩提高一样并不开朗。 华东地区变成注塑机业务流程闪光点 大同机械也留意到我国一部分销售市场明显改善,在其中以华东地区汽车零配件、家用电器及生活用品领域比较明显,该地域公司购买中、大中型注塑机十分积极主动,该商品已变成其无锡市加工厂旗舰级商品。 将来现金流量令人担忧 大同机械2016年上半年度财务报表显示信息,现钱降低933五万港币,现金余额仅有2.34亿港元。但其发布的资产重组计划支出中,仅测算了东莞市明新塑胶制品的1700万rmb花费。 而截止12月31日,再加上另一家企业的停止运营,和俩家工业厂房的提产,资产重组计划预估将花销1.25亿港元。 来源于:CPRJ 中国塑料硫化橡胶 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
- NORYL树脂光伏接线盒
- 2022-10-18 0
- NORYL树脂具有优秀的尺寸稳定性、电气和热性能,能耐受-40°C至140°C的温度,长期在户外的湿热环境使用后,还可保持85%以上的性能,且具有低翘曲特性,满足对接线盒材料的高要求
- 阅读全文
NORYL树脂光伏接线盒
2-长期在户外的湿热环境使用后,可保持85%以上的性能;
3-具有低翘曲特性,满足对接线盒材料的高要求,如设计的灵活性、无氯无溴阻燃、易安装性等;
4-可降低系统成本,符合严格的全球监管标准。
抱歉!暂无数据。